In the metallurgical production process, due to the liquid slag steel (iron) splashing at the mouth of the metallurgical container, the equipment is seriously bonded, making it difficult to clean the slag steel (iron), increasing the labor intensity. Moreover, the lining of the mouth of the container is seriously damaged during cleaning, leading to increased repair time, severely affecting smelting production efficiency, resulting in higher steelmaking costs.
Using the anti-slag spray coating produced by our company to spray the mouth of the metallurgical container can reduce the bonding amount of slag steel (iron) and make it easy to fall off during cleaning. It greatly reduces labor intensity, reduces cleaning times and time, extends the service life of metallurgical container linings, improves production efficiency, and reduces steelmaking costs.
| Anti-slag spray coating (magnesium) | |||||
| indicators | MgO | SiO2 | Binding agent | Synergist | Granularity |
| ≥32 | ≤25 | 15-30 | 10-25 | ≤1mm | |
| Suitable for: ladle edge, ladlefurnace cover, converter mouth, VD furnace cover. | |||||
| Anti-slag spray coating (aluminum) | |||||
| indicators | SiO2 | AL2O3 | Binding agent | Synergist | Granularity |
| ≥30 | ≥25 | 15-30 | 10-25 | ≤1mm | |
| Suitable for: Slag basin, slag tank, ladle, oxygen gun | |||||